Technical informations

  Zinc alloy according to EN12844
Property Unit ZP0400 ZP0410 ZP0430 ZP0810
Mechanical properties
Yield Strength MPa 268 295 361 319
Ultimate tensile strength (UTS) MPa 308 331 397 387
Young's modulus GPa 96 96 96 96
Torsional modulus GPa >33 >33 >33 >33
Elongation at Fmax % 3 2 3 4
Elongation at fracture % 6,3 3,6 6 8
Shear strength MPa 214 262 317 275
Compressive yield stress MPa 414 600 641 ∼600
Impact strength Joules 46 52 38 42
Fatigue resistance (5 x108) MPa 48 57 59  
Hardness Brinell HB Brinell 97 114 130 110
Fracture toughness KIC x107N.m-3/2 2,25 2,1   1,95
Specific damping capacity @ 35 MPa % 18 19 19 20
Specific damping capacity @ 100 MPa % 40 41 42 44
Physical properties (at 20°C)
Density g cm-3 6,7 6,7 6,8 6,3
Coefficient of thermal expansion x10-6 °C-1 27,4 27,4 27,8 23,3
Thermal conductivity W m-1hr-1m-2 113 109 105 112
Electrial conductivity % IACS 27 26 25 27,7
Electrical resistivity μohm cm 6,37 6,54 6,85 6,2
Melting temeperature range °C 381-387 380-386 379-390 375-404
Casting temperature °C 415-435 415-435 415-435  
Shrinkage % 0,4-0,6 0,4-0,6 0,4-0,6 0,7
Specific heat capacity J kg-1 °C-1 419 419 419 435
friction coeffient - 0,07 0,08 0,08 0,11
Chemical composition
  Norm EN12844 EN12844 EN12844 EN12844
  % Al 3,7-4,3 3,7-4,3 3,7-4,3 8,0-8,8
  % Cu <0,05 0,7-1,25 2,7-3,3 0,9-1,1
  % Mg 0,02-0,06 0,02-0,06 0,02-0,06 0,015-0,03
  % Zn Rest Rest Rest Rest
  % Fe <0,05 <0,05 <0,05 <0,05
  % Si <0,03 <0,03 <0,03 <0,045
  % Ni <0,02 <0,02 <0,02 <0,02
  % Sn <0,002 <0,002 <0,002 <0,003
  % Cd <0,005 <0,005 <0,005 <0,006
  % Pb <0,005 <0,005 <0,005 <0,006
Other alloy designations
  Zamak 3 Zamak 5 Zamak 2 ZA 8
  ZP3 ZP5 ZP2 ZP8
  ZnAl4 ZnAl4Cu1 ZnAl4Cu3 ZnAl8Cu1
  Z410 Z410 Z430 Z810